Rare-earth regenerator material particles, and group of rare-earth regenerator material particles, refrigerator and measuring apparatus using the same, and method for manufacturing the same

ABSTRACT

Provided is a group of rare-earth regenerator material particles having an average particle size of 0.01 to 3 mm, wherein the proportion of particles having a ratio of a long diameter to a short diameter of 2 or less is 90% or more by number, and the proportion of particles having a depressed portion having a length of 1/10 to ½ of a circumferential length on a particle surface is 30% or more by number. By forming the depressed portion on the surface of the regenerator material particles, it is possible to increase permeability of an operating medium gas and a contact surface area with the operating medium gas.

This application is a Divisional of U.S. application Ser. No. 15/369,546filed on Dec. 5, 2016, Divisional of U.S. application Ser. No.13/391,831 filed on Feb. 23, 2012, which is a National Stage ofapplication PCT/JP10/064180, filed on Aug. 23, 2010.

TECHNICAL FIELD

The present invention relates to regenerator material (cold accumulatingmaterial) particles and a group of regenerator material particles, andparticularly relates to a rare-earth regenerator material, arefrigerator and a measuring apparatus using the regenerator material,and a method for manufacturing the regenerator material.

BACKGROUND ART

In the field of superconducting technology used in a magnetic floatingtrain, a fracture diagnostic apparatus based on nuclear magneticresonance, or the like, cryogenic technology has been progressedremarkably for various applications including a cryopump used in anultra-high vacuum apparatus such as a VLSI pattern transfer apparatus.As it has come to the stage of putting the cryogenic technology topractical use, a smaller refrigerator having a higher performance hasbeen progressively developed and realized practically. Especially, thereis increasing importance in freezing and cooling techniques fordeveloping an environment having a temperature around the absolute zerotemperature (−273° C.) at which the cryopump for creating a high vacuumatmosphere in a superconducting magnet or a semiconductor manufacturingapparatus is operated, and there is a strong demand for a refrigeratorexhibiting a high reliability and excellent characteristics.

Conventionally, in a superconducting MRI (nuclear magnetic resonanceimaging) apparatus (image measuring apparatus) used for taking tomogramsin the medical field, a small refrigerator using helium, such as aGifford MacMahon type refrigerator (GM refrigerator) has been employedin order to cool and refrigerate the superconducting magnet.

The GM refrigerator is composed of combination of a compressor forcompressing He gas, an expansion unit for expanding the compressed Hegas, and a regenerator unit (cold accumulating unit) for keeping the Hegas cooled in the expansion unit in the cooled state. In therefrigerator, the He gas compressed by the compressor is expanded to becooled by about 60 cycles per minute, and then, a system to be cooled iscooled through a tip end portion of the expansion unit of therefrigerator.

Alternatively, there have been developed pulse tube refrigerators inrecent years. The pulse tube refrigerator is a refrigerator in whichhigh-pressure He gas is provided to the refrigerator in a prescribedperiod. Since the pulse tube refrigerator has a smaller vibration incomparison with the GM refrigerator, the pulse tube refrigerator has theadvantage of suppressing noise generation at measurement in, forexample, an MRI apparatus.

In refrigerators used for any purpose, the regenerator unit is filledwith a regenerator material (cold accumulating material). As theregenerator material for refrigerator used in an extremely lowtemperature region around the absolute zero temperature, for example, of10K or less, further of 4K or less, a rare-earth regenerator materialdisclosed in Japanese Patent No. 2609747 (Patent Document 1) istechnically effective. The technique disclosed in the Patent Document 1involves adjusting the particle size and the aspect ratio of rare-earthregenerator material particles, and thereby enables high-density fillingof the regenerator material particles.

On the other hand, studies for employing multi-staged regenerator unitshave been made in view of improving performance of the refrigerator. Forexample, Japanese Patent Laid-Open No. 2001-272126 (Patent Document 2)discloses a two-staged pulse tube refrigerator. By employingmulti-staged regenerator units, it is possible to attain a highercooling velocity (refrigerating speed). It is also possible to attain alarger cooling amount, thereby the refrigerator can be installed in alarger-scaled apparatus. By employing the multi-staged regeneratorunits, He gas must be supplied in a larger amount at a higher pressure.

The refrigerating performance of a refrigerator depends on amount of Hegas having contact with the surface of the regenerator materialparticles. As the regenerator material particles, particles having aspherical shape have been conventionally used in view of realizinghigh-density filling, and therefore, it is difficult to fill theparticles at a higher density than ever before. Although there is aconceivable measure of filling the space between the regeneratormaterial particles with smaller regenerator material particles, fillingparticles in an excessively large amount leads to a decrease inpermeability of He gas serving as a cooling medium. Another measure offilling the particles under a high pressure is also conceivable;however, filling under an excessively high pressure leads to crushing ofthe regenerator material particles, which rather causes clogging in acooling system. Therefore, there is a technical demand for a regeneratormaterial capable of ensuring the high-density filling and attaining alarger contact surface area with the He gas.

CITATION LIST Patent Document

-   Patent Document 1: Japanese Patent No. 2609747-   Patent Document 2: Japanese Patent Laid-Open No. 2001-272126

SUMMARY OF INVENTION Problems to be Solved by the Invention

The present invention has been made to solve the above describedproblems and an object of the present invention is to provide rare-earthregenerator material particles capable of ensuring high-density fillingand attaining a larger contact surface area with an operating medium gassuch as He gas. Another object of the present invention is to provide amethod for effectively manufacturing the rare-earth regenerator materialparticles having a larger contact specific surface area.

Means for Solving the Problems

The present invention provides a group of rare-earth regeneratormaterial particles having an average particle size of 0.01 to 3 mm,wherein the proportion of particles having a ratio of a long diameter toa short diameter of 2 or less is 90% or more by number, and theproportion of particles having a depressed portion having a length of1/10 to ½ of a particle circumferential length on a particle surface is30% or more by number.

Moreover, it is preferable that the depressed portion has a depth of1/10 or less of a particle diameter. Furthermore, it is preferable thatthe rare-earth regenerator material particles are composed of at leastone selected from Nd, Er₃Ni, and HoCu₂.

The present invention provides rare-earth regenerator materialparticles, having a particle size of 0.01 to 3 mm, having a ratio of along diameter to a short diameter of 2 or less, and having a depressedportion having a length of 1/10 to ½ of a particle circumferentiallength on a particle surface.

The group of rare-earth regenerator material particles described aboveis suitable for use in a refrigerator comprising a regenerator container(cold accumulating unit) filled with the group of rare-earth regeneratormaterial particles. In addition, it is preferable that the regeneratorcontainer comprises two or more stages of regenerator material-filledzones through a mesh material.

The group of rare-earth regenerator material particles described aboveis suitable for use in a measuring apparatus comprising asuperconducting magnet comprising the refrigerator. In addition, it ispreferable that the measuring apparatus is at least one of an MRI(magnetic resonance imaging apparatus) and an NMR (nuclear magneticresonance analyzer).

The present invention provides a first method for manufacturing a groupof rare-earth regenerator material particles, comprising a step ofpreparing a molten metal containing a rare-earth element, a step ofsupplying the molten metal to a rotary disk having a rotating velocityof 7000 to 11000 rpm in a chamber under an argon atmosphere, and a stepof rapidly cooling (quenching) the molten metal having a granular formflipped by the rotary disk. In addition, it is preferable that themolten metal is supplied through a jetting hole having a diameter of0.05 to 2 mm. Moreover, it is preferable that the rotary disk is made ofceramic. Furthermore, it is preferable that the molten metal is suppliedafter preliminarily heating the rotary disk to a temperature of 800° C.or more.

The present invention provides a second method for manufacturing a groupof rare-earth regenerator material particles, comprising a step ofpreparing a molten metal containing a rare-earth element, a step ofjetting the molten metal from a rotary nozzle having a rotating velocityof 7000 to 11000 rpm in a chamber under an argon atmosphere, and a stepof rapidly cooling (quenching) the molten metal having a granular formjetted from the rotary nozzle. In addition, it is preferable that themolten metal is supplied through a jetting hole having a diameter of0.05 to 2 mm. Furthermore, it is preferable that the molten metal isjetted after preliminarily heating the rotary nozzle to a temperature of800° C. or more.

Advantages of the Invention

According to the group of rare-earth regenerator material particles ofthe present invention, it is possible to ensure high-density filling(packing) and attain a larger contact surface area between the group ofregenerator material particles and an operating medium gas such as Hegas. As a result, characteristics of the refrigerator using the group ofregenerator material particles and characteristics of the measuringapparatus using the refrigerator can be greatly improved.

According to the method for manufacturing the group of rare-earthregenerator material particles of the present invention, it is possibleto manufacture the group of rare-earth regenerator material particles ofthe present invention effectively. By using the rare-earth regeneratormaterial particles of the present invention, it is possible to form thegroup of rare-earth regenerator material particles effectively.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1A is a perspective view illustrating one example of rare-earthregenerator material particle of the present invention and FIG. 1B is amagnified cross sectional view taken in the direction of the arrowsalong the line B-B in FIG. 1A.

FIG. 2 is a perspective view illustrating another example of rare-earthregenerator material particles of the present invention.

FIG. 3 is a cross sectional perspective view illustrating one example ofa method for manufacturing the rare-earth regenerator material particlesof the present invention.

FIG. 4 is a cross sectional perspective view illustrating anotherexample of a method for manufacturing the rare-earth regeneratormaterial particles of the present invention.

FIG. 5 is a cross sectional view illustrating one example of aconfiguration of a GM refrigerator.

DESCRIPTION OF EMBODIMENTS

A group of rare-earth regenerator material particles of the presentinvention is a group of rare-earth regenerator material particles havingan average particle size of 0.01 to 3 mm, in which the proportion ofparticles having a ratio of a long diameter to a short diameter of 2 orless is 90% or more by number, and the proportion of particles having adepressed portion having a length of 1/10 to ½ of a particlecircumferential length on a particle surface is 30% or more by number.

The rare-earth regenerator material comprises a rare-earth element as aconstituent element. Examples of the rare-earth element may include atleast one or two or more selected from Y (yttrium), La (lanthanum),cerium (Ce), praseodymium (Pr), neodymium (Nd), promethium (Pm),samarium (Sm), europium (Eu), gadolinium (Gd), terbium (Tb), dysprosium(Dy), holmium (Ho), erbium (Er), thulium (Tm), and ytterbium (Yb).

Examples of the rare-earth regenerator material may be composed of arare-earth elemental of single substance, an alloy with Cu (including anintermetallic compound), an alloy with Ni (including an intermetalliccompound), a rare-earth oxide (including a rare-earth complex oxide),and a rare-earth sulfide. Examples of a constituent material of therare-earth regenerator material particles include Nd, Er₃Ni, ErNi,HoCu₂, Gd₂O₃, and Gd₂O₂S.

The group of rare-earth regenerator material particles has an averageparticle size of 0.01 to 3 mm. When the average particle size is lessthan 0.01 mm, the regenerator material particles filled in a regeneratorcontainer have an excessively small space therebetween, which leads to adecrease in permeability of an operating medium gas (He gas). On theother hand, when the average particle size exceeds 3 mm, the regeneratormaterial particles have an excessively large space therebetween, andtherefore, a sufficient contact surface area with the operating mediumgas cannot be ensured. It is more preferable that the group ofregenerator material particles has an average particle size of 0.1 to0.5 mm. When the average particle size is in the above range, both ofthe permeability of the operating medium gas and the contact surfacearea can be increased. The average particle size of the group ofregenerator material particles is measured by a particle sizedistribution analyzer. A particle size D of the respective regeneratormaterial particles is determined as (short diameter S+long diameterL)/2.

Moreover, in the group of regenerator material particles of the presentinvention, the proportion of particles having a ratio of the longdiameter to the short diameter of 2 or less is defined as 90% or more bynumber. 90% or more by number of particles having an aspect ratio (L/S)of 2 or less indicates that the proportion of particles having aspherical shape close to a real spherical shape is large. When theproportion of particles having a spherical shape is large, theregenerator material particles can have point contact with each other,thereby the contact surface area between the group of regeneratormaterial particles and the operating medium gas can be increasedlargely.

It is noted that when the proportion of regenerator material particleshaving a large aspect ratio is large, variation (scattering) in thespace between the particles occurs, which leads to a decrease in thepermeability of the operating medium gas, even if the rare-earthregenerator material particles have an average particle size of 0.01 to3 mm. Furthermore, for example, when the particles having a large aspectratio and then having an elongated shape are contained, a larger amountof the particles have contact with each other not at point but onsurface, which reduces the contact surface area with the operatingmedium gas. As a result, the proportion of the particles having anaspect ratio of 2 or less is more advantageously higher, and ispreferably 95% or more, more preferably of 100%.

The proportion of the regenerator material particles having an aspectratio (long diameter/short diameter) of 2 or less is measured by thefollowing procedure. A magnified picture of 200 particles of theregenerator material particles is taken, the long diameter L and theshort diameter S of the respective regenerator material particles in thepicture are measured as shown in FIG. 1A, the number of particles havingan aspect ratio (L/S) of 2 or less is counted, and the objectiveproportion is determined by the formula below.(number of particles having an aspect ratio of 2 or less/200)×100(%)

In the present invention, the group of rare-earth regenerator materialparticles having the aforementioned average particle size and theaforementioned aspect ratio is further characterized in that theproportion of particles having a depressed portion having a length of1/10 to ½ of a particle circumferential length on a particle surface is30% or more by number. Here, the particle circumferential length isdefined as an equatorial length (πD) of the spherical particle havingthe particle size described above.

FIGS. 1 and 2 show examples of regenerator material particles 1 havingdepressed portions 2 and 3. In FIGS. 1A and 1B, a channel-shapeddepressed portion 2 is formed on a surface of the rare-earth regeneratormaterial particle 1 in a range having a length R. In FIG. 2, ahole-shaped depressed portion 3 is formed on a surface of the rare-earthregenerator material particle 1 having a length R. It is noted that theshape of the depressed portion can be selected from various shapesincluding a channel shape and a hole shape. In the case of forming thehole-shaped depressed portion 3 having a length R shown in FIG. 2 inplural numbers, a total of lengths R1, R2, and—which are the length ofdepressed portions 3, 3, and—respectively is taken as “the length R ofthe depressed portion”.

The length R of the depressed portion is set to be a length of 1/10 to ½of the circumferential length (πD) on the particle surface. When thelength R of the depressed portion is less than 1/10 of thecircumferential length, the depressed portion becomes excessively smalland the surface area of the regenerator material particles cannot beincreased.

On the other hand, when the length R of the depressed portion exceeds ½of the particle circumferential length, the depressed portion becomesexcessively large, which leads to a decrease in structural strength ofthe regenerator material particles. If the structural strengthdecreases, there may be posed a problem that the regenerator materialparticles are liable to be easily broken by impact or vibrationresulting from action for filling the regenerator material particlesinto the regenerator container or from operation of a refrigerator. Thelength R of the depressed portion is more preferably 1/10 to ⅓ of theparticle circumferential length.

Although the depressed portion may be formed in plural numbers, thenumber of the depressed portion per one regenerator material particle is2 or less, preferably 1 because an excessive amount of the depressedportion leads to a decrease in the structural strength of theregenerator material particles. In addition, as shown in FIG. 1B, when adepth d of the depressed portion 2 is excessively large, the structuralstrength of the regenerator material particles 1 decreases, even if thenumber of the depressed portion 2 is 1. Therefore, it is preferable thatthe depth d of the depressed portion is 1/10 or less of the diameter(the particle size D) of the regenerator material particles 1.

The length R of the depressed portion is measured by the followingprocedure. A magnified picture of the respective regenerator materialparticles 1 is taken, and the diameter D of the particle 1 and thelength R of the depressed portion in the picture are measured. It isnoted that, in the case of regenerator material particles having anelliptic shape, the circumferential length (πD) is obtained by taking(long diameter L+short diameter S)/2 as the diameter D. Also, as for thedepth d of the depressed portion 2, 3, a method using a magnifiedpicture is available. An example of such a method includes a methodusing an AFM magnifying glass (microscope).

In the present invention, the regenerator material particles 1 havingthe aforementioned depressed portions 2, 3 is contained at a proportionof 30% or more based on the total number of the particles. The number ofthe regenerator material particles having the depressed portion ismeasured by the following procedure. A magnified picture of 200particles is taken, the number of the regenerator material particleshaving the depressed portion in the picture is measured, and theobjective number is determined by the formula (number of regeneratormaterial particles having depressed portion/200)×100(%). This procedureis performed on another 200 particles three times, and an averagethereof is taken as the proportion, by number, of the particles havingthe depressed portion.

When the proportion of the regenerator material particles having thedepressed portion is less than 30% by number, an increase in the contactsurface area between the regenerator material particles and theoperating medium gas is small. It is more preferable that the proportionof the regenerator material particles having the prescribed depressedportion is 50% or more and 100% or less by number.

The group of rare-earth regenerator material particles in which theproportion, by number, of the regenerator material particles having theprescribed depressed portion is adjusted as mentioned above is suitablefor use in a refrigerator for providing an environment having atemperature in an extremely low temperature region of 10K or less,further of 4K or less.

The refrigerator comprises a regenerator container (cold accumulatingunit) for filling regenerator material particles. The refrigeratorcomprises the regenerator container filled with the aforementionedregenerator material particles. It is also possible to employ amulti-staged refrigerator by connecting two or more regeneratorcontainers or by forming two or more regenerator material-filled zonesthrough a mesh material in the regenerator container. In themulti-staged refrigerator, a volume of the regenerator material-filledzone can be increased because of the multi-staged configuration, therebyrefrigerating performance can be improved drastically.

In the refrigerator of the present invention, the regenerator containeris filled with the group of rare-earth regenerator material particles ofthe present invention, in the case of a one-staged refrigerator. In thecase of the multi-staged refrigerator, at least one of the regeneratormaterial-filled zones (cooling stages) is filled with the group ofrare-earth regenerator material particles of the present invention. Inthe multi-staged refrigerator, although it is preferable to fill all ofthe regenerator material-filled zones with the group of rare-earthregenerator material particles of the present invention, anotherregenerator material-filled zone may be filled with another type ofregenerator material depending on refrigerating performance required. AnExample of another type of regenerator material may include meshmaterial comprising a metal mesh material composed of copper, a copperalloy, or the like.

The refrigerating performance of the refrigerator depends on howeffective the operating medium gas such as He gas has contact with theregenerator material particles. In the group of rare-earth regeneratormaterial particles of the present invention, the particles have aspherical shape with the depressed portion formed thereon, thereby thehigh-density filling of the regenerator material particles can beensured, resistance to permeation (flow resistance) of the operatingmedium gas is not increased, and the contact surface area between theoperating medium gas and the regenerator material particles can beincreased. Especially, such a refrigerator is suitable for use as arefrigerator in which the operating medium gas moves back and forth witha high pressure such as the multi-staged refrigerator.

Also, such a refrigerator is suitable for use as a refrigerator foroperating a superconducting magnet. Superconducting technology is usedin a magnetic floating train, a nuclear magnetic resonance apparatus,and the like. Especially, the nuclear magnetic resonance apparatus isused in a wide variety of applications including an MRI apparatus for ahuman body, an NMR apparatus for a non-human body. Moreover, such arefrigerator can be also applied in a cryopump used for a semiconductormanufacturing apparatus. In any of the above cases, the refrigeratingperformance of the refrigerator can be improved, which leads toimprovement in reliability and characteristics of the measuringapparatus.

Next, a description is given of a method for manufacturing a group ofrare-earth regenerator material particles of the present invention. Anexample of the method for manufacturing a group of rare-earthregenerator material particles of the present invention includes amethod of mixing the rare-earth regenerator material particles havingthe depressed portion and rare-earth regenerator material particles nothaving the depressed portion in specified amounts.

As a method other than the above method, an effective method formanufacturing the group of rare-earth regenerator material particles ofthe present invention is described below.

FIG. 3 shows one example of the manufacturing method. FIG. 3 is a crosssectional perspective view illustrating a configuration of amanufacturing apparatus based on Rotary Disc Process (RDP) in which amolten metal is dispersed by a disk-shaped rotary body and thensolidified. The manufacturing apparatus comprises a cooling chamber 9, adisk-shaped rotary body 10, a ladle 11, a molten metal 12, a pouringnozzle 13, (a group of) rare-earth regenerator material particles 14,and a particle collection vessel 15.

In the rapid cooling (quenching) apparatus using a rotary disk based onthe Rotary Disc Process shown in FIG. 3, first, a molten metalcomprising the rare-earth element and another component as needed inspecified amounts is prepared. Another component is Ni in the case ofEr₃Ni and Cu in the case of HoCu₂. That is, the molten metal containingthe same constituent element as that of the objective rare-earthregenerator material is prepared.

The molten metal 12 is poured into the ladle 11, and then, supplied tothe disk-shaped rotary body (rotary disk) 10 from the pouring nozzle 13.The molten metal 12 is flipped on the disk-shaped rotary body 10rotating at a high velocity, and then, falls in the cooling chamber 9with being cooled and solidified rapidly to be the rare-earthregenerator material particles 14. The rare-earth regenerator materialparticles 14 fall into the particle collection vessel 15, thus formingthe group of rare-earth regenerator material particles.

In order to manufacture the group of regenerator material particleshaving an average particle size of 0.01 to 3 mm, it is preferable to seta diameter of a jetting hole formed on the pouring nozzle to 0.05 to 2mm. Moreover, it is preferable that the disk-shaped rotary body 10 has arotating velocity of 7000 to 11000 rpm. The average particle size of theobtained rare-earth regenerator material particles is controlled byadjusting the rotating velocity and the size of the jetting hole(pouring nozzle 13).

In the above manufacturing method, it is preferable that the disk-shapedrotary body 10 has a high rotating velocity of 7000 rpm or more. On theother hand, an upper limit of the rotating velocity is preferably 11000rpm because an excessively large rotating velocity facilitates formationof regenerator material particles having an aspect ratio more than 2.

It is preferable that the molten metal 12 flipped by the disk-shapedrotary body 10 is rapidly cooled (quenched) in an argon atmosphere. Byemploying the argon atmosphere, it is possible to inhibit mixing in ofan impurity gas component (oxygen or nitrogen). Nitrogen gas cannot beused as the atmosphere of the cooling chamber because nitrogen gasreacts with the molten metal when used as an inert gas. For the samereason, air cannot be also used.

The molten metal 12 after dispersed is cooled at such a rate that atemperature is lowered from 1000° C. to room temperature in 10 secondsor less, preferably in 5 seconds or less. There may be a case where aninitial temperature of the molten metal 12 may exceed 1000° C. becausethe temperature of the molten metal 12 varies depending on the material.Furthermore, it is preferable that an interior of the cooling chamber 9is coated with a heat resistant resin. By employing the coating using aresin, it is possible to inhibit mixing in of an impurity metal when therare-earth regenerator material particles have contact with theinterior. In the same manner, it is also preferable that an interior ofthe particle collection vessel 15 is coated with a resin. By inhibitingmixing in of the impurity gas component and the impurity metalcomponent, it is possible to attain such a small content as a oxygencontent of 100 ppm or less, a nitrogen content of 20 ppm or less, an Alcontent of 50 ppm or less, and a Si content of 30 ppm or less.

In the above method for manufacturing the group of rare-earthregenerator material particles of the present invention, the moltenmetal 12 is supplied to the rotary disk rotating at a high velocity of7000 to 11000 rpm from the pouring nozzle 13 comprising the jetting holehaving a diameter of 0.05 to 2 mm. The molten metal having a granularform flipped by the rotary disk 10 is cooled rapidly. The molten metalhaving a granular form flipped swiftly by the rotary disk 10 rotating ata prescribed rotating velocity is rapidly cooled with keeping thegranular form. At this point, the molten metal having a granular form israpidly cooled from its direction of movement after flipped. Since thecooling chamber 9 is sealed with the argon atmosphere, the molten metalhaving a granular form is formed into the rare-earth regeneratormaterial particles 14 with being subjected to flow resistance of theargon atmosphere.

Here, since the molten metal having a granular form is subjected to theflow resistance, the particle is dispersed and cooled with engulfing theargon gas on the back of its direction of movement, and the engulfmentof the argon gas causes the channel-shaped depressed portion. Therefore,it is possible to control the shape of the channel-shaped depressedportion 2 by adjusting the rotating velocity of the rotary disk 10 andthe diameter of the pouring nozzle 13 related to an input amount of themolten metal 12. In addition, the hole-shaped depressed portion 3 shownin FIG. 2 is formed by instant collision between the molten metalshaving a granular form during dispersion and cooling of the flippedmolten metals having a granular form.

In addition, it is preferable that the rotary disk 10 is made ofceramic. Examples of the ceramic may include alumina (Al₂O₃) and boronnitride (BN). When the rotary disk 10 is made of a metal, there is afear that a metal impurity is mixed in the rare-earth regeneratormaterial.

Moreover, it is preferable that the molten metal 12 is supplied afterpreliminarily heating the rotary disk 10 to a temperature of 800° C. ormore. When the rotary disk 10 is not heated, the molten metal 12 israpidly cooled at the moment when the molten metal 12 comes in contactwith the rotary disk 10, and the molten metal 12 adheres to the rotarydisk 10. In order to flip the molten metal 12 smoothly and uniformly, itis preferable to preliminarily heat the rotary disk 10 to a temperatureof 800° C. or more. It is noted that although there is no restriction onan upper limit of a temperature of the preliminary heating, the upperlimit is preferably 1000° C. When the temperature of the preliminaryheating is excessively high, there is a fear that the cooling chamber 9comes to have a high temperature because the rotary disk 10 may beinstalled in the cooling chamber 9 as shown in FIG. 3, and the rapidlycooling step (quenching step) of the molten metal 12 is performedinsufficiently.

Examples of the method of the preliminary heating may include a methodof installing a heater to the rotary disk 10 and a method ofpreliminarily heating the rotary disk 10 by bringing the rotary disk 10into contact with the molten metal 12 which is a raw material of therare-earth regenerator material particles for a certain period of time.Also in view of the need of the preliminary heating, it is preferablethat the rotary disk 10 is made of ceramic.

Furthermore, the rotary disk 10 has a diameter preferably of 20 to 100mm. When the diameter is less than 20 mm, the rotary disk is small, andtherefore, there is a possibility that the molten metal 12 directlyfalls without touching the rotary disk 10 unless the molten metal 12 issupplied after accurately aligned the position. Especially, in the caseof installing the particle collection vessel 15 at the bottom of thecooling chamber 9, attention has to be paid because an obtained productbecomes defective. On the other hand, when the diameter of the rotarydisk 10 exceeds 100 mm, there is a fear that the rotary disk 10 comes tohold an excessive heat by the preliminary heating, and then, the coolingchamber 9 is heated, which results in an adverse effect on the coolingstep.

FIG. 4 shows another example of the manufacturing method. FIG. 4 is across sectional perspective view illustrating a configuration of anapparatus for manufacturing a group of regenerator material particlesbased on rotary nozzle process in which a molten metal is dispersed by arotary nozzle 21 having a jetting hole 22 and then solidified. Themanufacturing apparatus comprises a cooling chamber 9, a ladle 11, amolten metal 12, (a group of) rare-earth regenerator material particles14, a rotary nozzle 21, and a jetting hole 22.

The molten metal is prepared by the same process as that describedabove.

At a side surface of the rotary nozzle 21, a small hole (jetting hole)22 is formed. The molten metal 12 dashes out from the jetting hole 22 asa molten metal having a droplet form by rotating the rotary nozzle 21 ata high velocity. The molten metal 12 after dashing out from the jettinghole 22 falls in the cooling chamber 9 with being rapidly cooled to bethe rare-earth regenerator material particles 14. The rare-earthregenerator material particles 14 fall into a particle collection vessel(not shown), thus forming the group of rare-earth regenerator materialparticles 14.

In order to manufacture the group of regenerator material particles 14having an average particle size of 0.01 to 3 mm, it is preferable to seta diameter of the jetting hole 22 formed on the rotary nozzle 21 to 0.05to 2 mm. Moreover, it is preferable that the disk-shaped rotary nozzle21 has a rotating velocity of 7000 to 11000 rpm. The average particlesize of the obtained rare-earth regenerator material particles iscontrolled by adjusting the rotating velocity and the size of thejetting hole 22. An upper limit of the rotating velocity is preferably11000 rpm because an excessively large rotating velocity of the rotarynozzle 21 facilitates formation of regenerator material particles havingan aspect ratio more than 2.

It is preferable that the molten metal 12 having a granular form afterdashing out from the jetting hole 22 is rapidly cooled (quenched) in anargon atmosphere. By employing the argon atmosphere, it is possible toinhibit mixing in of an impurity gas component (oxygen or nitrogen). Themolten metal having a granular form 12 is cooled at such a rate that atemperature is lowered from 1000° C. to room temperature in 10 secondsor less, preferably in 5 seconds or less. It is noted that an initialtemperature may exceed 1000° C. because the temperature of the moltenmetal varies depending on the material. Moreover, it is preferable thatan interior of the cooling chamber 9 is coated with a heat resistantresin. By employing the coating using a resin, it is possible to inhibitmixing in of an impurity metal when the rare-earth regenerator materialparticles have contact with the interior. In the same manner, it is alsopreferable that an interior of the particle collection vessel is coatedwith a resin. By inhibiting mixing in of the impurity gas component andthe impurity metal component, it is possible to attain such a smallcontent as an oxygen content of 100 ppm or less, a nitrogen content of20 ppm or less, an Al content of 50 ppm or less, and a Si content of 30ppm or less.

Even in the case of using the rapidly cooling apparatus based on rotarynozzle comprising the rotary nozzle 21 as shown in FIG. 4, it ispreferable to preliminarily heat the rotary nozzle 21 to a temperatureof 800° C. or more. By means of preliminary heating, it is possible toprevent the molten metal 12 from being cooled beyond necessity in therotary nozzle 21. Although there is no restriction on an upper limit ofa temperature of the preliminary heating for the rotary nozzle 21, theupper limit is preferably 1000° C. When the temperature of thepreliminary heating is excessively high, there is a fear that thecooling chamber 9 comes to have a high temperature because the rotarynozzle 21 may be installed in the cooling chamber 9, and then, therapidly cooling step is performed insufficiently.

In the method based on rotary nozzle, it is possible to manufacture alager amount of the regenerator material particles at one time incomparison with the method based on rotary disk by forming a pluralityof jetting holes 22 at the side surface of the rotary nozzle 21. Therotary nozzle 21 has a diameter preferably of 10 to 50 cm.

In the method for manufacturing a group of regenerator materialparticles of the present invention, there often exist the particleshaving the depressed portion and particles not having the depressedportion. In order to extract only the rare-earth regenerator materialparticles having the depressed portion from the group of the particles,a method of screening by rolling the particles at a specified inclinedsurface is available. When the depressed portion is formed on theparticle surface, the particle rolls down at a higher velocity incomparison with the particle without the depressed portion because asurface friction becomes slightly smaller. It is also possible to screenby using the difference in the falling velocity.

When it is difficult to apply the rapid cooling and solidifying methodin the case of rare-earth oxide particles, rare-earth oxysulfideparticles, and the like, a method of polishing a surface of a sinteredbody obtained by a sintering process to obtain specified particles andthen forming the depressed portion required can be applied.

EXAMPLES Examples 1 to 6 and Comparative Example 1

A molten metal was prepared by using Ho and Cu at a ratio correspondingto HoCu₂. Next, droplets of the molten metal 12 was supplied on aceramic rotary disk 10 from a pouring nozzle 13 and then flipped by theceramic rotary disk 10 in a rapidly cooling (quenching) apparatus basedon rotary disk shown in FIG. 3, thus manufacturing groups of rare-earthregenerator material particles 14 of the Examples and the ComparativeExample. It is noted that a rapidly cooling operation was performedunder an argon atmosphere at such a cooling rate that the temperaturewas lowered from 1000° C. to room temperature in 5 seconds or less. Themanufacturing process was performed on the conditions shown in Table 1including a shape of the pouring nozzle (a diameter of a jetting hole)and a rotating velocity of the rotary disk. A cooling chamber 9 with aninterior coated with a resin was used.

In Comparative Example 1, the manufacturing process was performed on thecondition of a lower rotating velocity of 2000 rpm.

TABLE 1 Pouring Nozzle Rotary Disk Diameter of Rotation Pre-heatingJetting Hole Diameter Velocity Temperature Sample No. (mm) (mm) (rpm) (°C.) Example 1 1.5 35 9000 970 Example 2 1.5 35 8000 900 Example 3 1.5 5011000 1000 Example 4 0.5 50 9000 850 Example 5 2.0 80 9500 1050 Example6 1.5 30 7000 500 Comparative 1.5 50 2000 800 Example 1

For each of the groups of rare-earth regenerator material particlesmanufactured on the conditions shown in Table 1, the average particlesize, the proportion (proportion by number) of regenerator materialparticles having an aspect ratio of 2 or less, and the proportion(proportion by number) of particles having a depressed portion having alength of 1/10 to ½ of a circumferential length on a particle surfacewere measured. Each of the parameters was measured by the aforementionedprocedure. The results are shown in Table 2.

TABLE 2 Proportion of Particles Having Average Depressed Portion HavingLength Depth d of Particle Proportion of Particle Having of 1/10 to ½ ofCircumferential Depressed Portion/ Size Aspect Ratio of 2 or less Lengthon Particle Surface Particle Diameter D Sample No. (μm) (Proportion byNumber %) (Proportion by Number %) (d/D) Example 1 200 100 80 1/10 orless Example 2 240 99 67 1/10 or less Example 3 130 96 95 1/10 or lessExample 4 45 98 84 1/10 or less Example 5 310 96 85 1/10 or less Example6 270 90 56 1/7 Comparative 550 75 10 1/10 or less Example 1

As is evident from the results shown in Tables 1 and 2, the groups ofregenerator material particles manufactured by the methods of theExamples of the present invention each had the prescribed depressedportion. In addition, it was confirmed that there existed both of achannel-shaped depressed portion and a hole-shaped depressed portion.Moreover, it was also confirmed that when the temperature of preliminaryheating (pre-heating) was lower as in Example 6, the particles have adepressed portion having a larger depth. On the contrary, when therotating velocity was small as in Comparative Example 1, the proportionof regenerator material particles having an aspect ratio of 2 or lesswas drastically decreased. Furthermore, in Comparative Example 1, thedepressed portion was formed in a smaller amount because argon wasengulfed in a smaller amount.

Examples 7 to 12 and Comparative Example 2

A molten metal was prepared by using Ho and Cu at a ratio correspondingto HoCu₂. Next, on the conditions and specifications of a rotary nozzleshown in Table 3, the molten metal 12 was supplied to a rotary nozzle 21from a pouring nozzle and jetted through a plurality of jetting holes 22formed on a side surface of the rotary nozzle 21, and then, rapidlycooled in an atmosphere gas in a rapidly cooling apparatus based onrotary nozzle shown in FIG. 4, thus manufacturing groups of rare-earthregenerator material particles of the Examples and the ComparativeExample. It is noted that the rapidly cooling operation was performedunder an argon atmosphere at such a cooling rate that the temperaturewas lowered from 1000° C. to room temperature in 5 seconds or less. Theconditions of a shape of the jetting hole and a rotating velocity wereshown in Table 3. A cooling chamber 9 with an interior coated with aresin was used.

TABLE 3 Rotary Nozzle Diameter of Rotation Pre-heating Jetting HoleDiameter Velocity Temperature Sample No. (mm) (cm) (rpm) (° C.) Example7 1.5 15 9500 930 Example 8 1.5 15 8500 950 Example 9 1.5 50 11000 820Example 10 0.5 30 9000 1000 Example 11 2.0 30 8000 970 Example 12 1.5 307200 450 Comparative 1.5 30 1500 800 Example 2

For each of the groups of rare-earth regenerator material particlesmanufactured on the conditions shown in Table 3, the average particlesize, the proportion (proportion by number) of regenerator materialparticles having an aspect ratio of 2 or less, the proportion(proportion by number) of particles having a depressed portion having alength of 1/10 to ½ of a circumferential length on a particle surface,and a ratio of a depth (d) of the depressed portion to a particle size(D) were measured. Each of the parameters was measured by theaforementioned procedure. The results are shown in Table 4.

TABLE 4 Proportion of Particles Having Average Depressed Portion HavingLength Depth d of Particle Proportion of Particles Having of 1/10 to ½of Circumferential Depressed Portion/ Size Aspect Ratio of 2 or lessLength on Particle Surface Particle Diameter D Sample No. (μm)(proportion by Number %) (Proportion by Number %) (d/D) Example 7 160 9645 1/10 or less Example 8 180 93 52 1/10 or less Example 9 140 90 621/10 or less Example 10 48 88 41 1/10 or less Example 11 230 84 38 1/10or less Example 12 170 80 34 ⅙ Comparative 200 90 8 1/10 or less Example2

As is evident from the results shown in Table 4, the groups ofrare-earth regenerator material particles of the Examples each had theprescribed depressed portion. In addition, it was confirmed that thereexisted both of a channel-shaped depressed portion and a hole-shapeddepressed portion. Moreover, it was also confirmed that when thetemperature of preliminary heating (pre-heating) was lower as in Example12, the particles had a depressed portion having a larger depth. On thecontrary, when the rotating velocity was small as in Comparative Example2, although the proportion of regenerator material particles having anaspect ratio of 2 or less was high, the depressed portion was formed ina smaller amount because argon was engulfed in a smaller amount.

In comparison with the method based on rotary disk, the proportion ofthe particles having a depressed portion was lower. This is because themethod based on rotary nozzle is a method in which the molten metal isjetted through the jetting hole in a granular form, whereas the methodbased on rotary disk is a method in which the molten metal is flipped bya disk rotating at a high velocity. The flipping operation is consideredto be more effective for forming the depressed portion.

Examples 13 to 24 and Comparative Example 3

A GM refrigerator is manufactured by filling the respective groups ofrare-earth regenerator material particles of Examples 1 to 12 andComparative Example 1 in a regenerator container (cold accumulatingunit) at a highest filling density (a filling rate of about 68%).

Here, a configuration of the GM refrigerator for a test is shown in FIG.5. As shown in FIG. 5, a GM refrigerator 30 is composed of externalcylinders 32 and 33 arranged in series in a vacuum chamber 31, a firstregenerator container 34 and a second regenerator container 35 installedto be movable back and forth in the external cylinders 32 and 33,respectively, a Cu mesh material 36 filled in the first regeneratorcontainer 34 as a first regenerator material, a second group ofregenerator material particles (1 c) of the Examples filled in thesecond regenerator container 35, and a compressor 37 for supplying Hegas into the external cylinder 32.

Seal rings 38 and 39 are installed between the external cylinders 32, 33and the first and the second regenerator containers 34, 35,respectively. In addition, a first expanding chamber 40 is formedbetween the external cylinder 32 and the first regenerator container 34and a second expanding chamber 41 is formed between the externalcylinder 33 and the second regenerator container 35. A first coolingstage 42 and a second cooling stage 43 are formed at the bottom of thefirst and the second expanding chambers 40 and 41, respectively.

Furthermore, in order to evaluate characteristics of the groups ofregenerator material particles prepared in the Examples and theComparative Example, a resistance thermometer 44 for measuring thetemperature of the second cooling stage 43 and a heater 45 forsubjecting a thermal load to the second cooling stage 43 are installedin the second cooling stage 43.

As the regenerator container, a cold accumulating unit having a size ofa diameter of 50 mm×a length of 80 mm (a stainless pipe having athickness of 1 mm) was used. For each of the refrigerators, permeabilityof an operating medium gas (He gas) and refrigerating performance(refrigerating capacity) were measured. The results are shown in Table5. Here, the permeability was measured by the following procedure. Afterthe refrigerator was operated for continuous 500 hours with supplying anoperating medium gas having a heat capacity of 25 J/K at a mass flowrate of 3 g/sec and a gas pressure of 16 atm, the mass flow rate of theoperating medium gas was measured. The permeability was represented by arelative value when the mass flow rate of Comparative Example 3 (arefrigerator using the regenerator material of Comparative Example 1) istaken as 100 (criterion value). A value larger than 100 indicates arelatively higher permeability.

The refrigerating performance of the group of regenerator materialparticles 1 c was measured by the following procedure. The group ofregenerator material particles 1 c was filled in the second regeneratorcontainer 35, while the Cu mesh material 36 was filled in the firstregenerator container 34, and the GM refrigerator 30 was operated at 60cycles per minute. He gas compressed to 20 atm by the compressor 37 wasadiabatically expanded repeatedly in the first expanding chamber 40 andthe second expanding chamber 41. The generated cold heats areaccumulated at the Cu mesh material 36 and the regenerator material 1 c.

The refrigerating performance in the examples was defined as a thermalload at the point when the temperature of the second cooling stage 43was elevated to stop at 6K with subjecting a thermal load to the secondcooling stage 43 by the heater 45 during operation of the refrigerator.The results are shown in Table 5.

TABLE 5 Group of Rare Earth Refrigerating Regenerator materialPeameability Performance Sample No.. Particles (Relative Value) (W)Example 13 Example 1 101 2.3 Example 14 Example 2 105 2.4 Example 15Example 3 90 2.6 Example 16 Example 4 102 2.2 Example 17 Example 5 1102.4 Example 18 Example 6 83 2.4 Example 19 Example 7 102 2.2 Example 20Example 8 101 2.2 Example 21 Example 9 92 2.5 Example 22 Example 10 1012.2 Example 23 Example 11 108 2.1 Example 24 Example 12 90 2.0Comparative Comparative 100 1.9 Example 3 Example 1 (Criterion Value)

As is evident from the results shown in Table 5, the refrigerators ofthe Examples each had an improved refrigerating performance. This isbecause the formed depressed portion increased the contact surface areabetween the rare-earth regenerator material particles and He gas. Thepermeability was inferior in Examples 15 and 21. This is because a groupof rare-earth regenerator material particles having a smaller averageparticle size in comparison with Comparative Example 3 was used in eachof these Examples.

Furthermore, breakage of the regenerator material particles after 500hours-operation was checked. The result was that no breakage was foundin the Examples except Examples 18 and 24, and the Comparative Example.It was confirmed that the strength of the regenerator material particleswas equal to or surpassing that of a conventional product.

On the other hand, in each of Examples 18 and 24, a slight crack wasfound in the regenerator material particle. As a result, it was foundthat the depth of the depressed portion was preferably 1/10 or less ofthe diameter.

Examples 25 to 27 and Comparative Example 4

Next, a two-staged pulse tube refrigerator was manufactured by using theregenerator material shown in Table 6, and the characteristics weremeasured by the same process. It is noted that the pulse tuberefrigerator is operated on the conditions of a He gas pressure of 2.3MPa at high pressure and a He gas pressure of 0.9 MPa at low pressure.As the regenerator container, a cold accumulating unit having a size ofa diameter of 50 mm×a length of 100 mm (a stainless pipe having athickness of 1 mm) was used.

TABLE 6 Regenerator Refrigerating Regenerator Material Material ofSecong Permeability Performance Sample No. of First Cooling StageCooling Stage (Relative Value) (W) Example 25 Mixed Particle of Example1 114 1.4 Example 1 + Pb particles having Average Particle Size of 500μm at Mixing ratio of 50:50 Example 26 Pb Particles Having AverageExample 4 116 1.2 Particle Size of 500 μm Example 27 Pb Particles HavingAverage Example 1 106 1.0 Particle Size of 500 μm Comparative PbParticles Having Average Comparative 100 0.7 Example 4 Particle Size of500 μm Example 1 (Criterion Value)

As is evident from the results shown in Table 6, the refrigerators usingthe regenerator materials of the Examples each had a higher permeabilityand an improved refrigerating performance. Especially, in Examples 25and 26 in which the group of rare-earth regenerator material particlesof the Example was used in both of the first and the second stages, anoutstanding refrigerating performance could be obtained.

Examples 28 to 30

Examples in which the rare-earth regenerator material particles werechanged to Nd, Er₃Ni, and ErNi were taken as Examples 28, 29, and 30,respectively, and the measurement was conducted by the same process. Asa manufacturing method, the method based on rotary disk which is thesame as in Example 1 was employed. The diameter of the jetting holeformed on the pouring nozzle, operation conditions and specifications ofthe rotary disk are shown in Table 7.

TABLE 7 Composition of Pouring Nozzle Rotary Disk Rare Earth Diameter ofRotation Pre-Heating Refregerator Jetting Hole Diameter VelocityTemperature Sample No. Material (mm) (mm) (rpm) (° C.) Example 28 Nd 1.340 9000 950 Example 29 Er₃Ni 1.6 40 9000 950 Example 30 ErNi 1.6 40 9000950

For each of the groups of rare-earth regenerator material particlesobtained in the Examples, the shape of the particles was measured by thesame process as that in the aforementioned Examples. The results areshown in Table 8.

TABLE 8 Proportion of Particles Having Average Depressed Portion HavingLength Depth d of Particle proportion of Particles Having of 1/10 to ½of Circumferencial Depressed Portion/ Size Aspect Ratio of 2 or lessLength on Particle Surface Particle Diameter Sample No. (μm) (Proportionby Number %) (Proportion by Number %) (d/D) Example 28 190 100 83 1/10or less Example 29 200 99 82 1/10 or less Example 30 190 96 78 1/10 orless

A refrigerator was manufactured by filling the respective groups ofrare-earth regenerator material particles obtained in Examples 28 to 30shown in Table 8 in a regenerator container of a GM refrigerator whichwas the same as that in Example 13. The permeability and therefrigerating performance were measured by the same process as that inExample 13. The results are shown in Table 9.

TABLE 9 Group of Rare Earth Refrigerating Refregerator PemeabilityPerformance Sample No. Material Particles (Relative value) (W) Example31 Example 28 101 3.4 Example 32 Example 29 103 3.6 Example 33 Example30 102 3.5 Comparative Comparative 100 1.9 Example 3 Example 1(Criterion Value)

As is evident from the results shown in Table 9, the refrigerators usingthe groups of regenerator material particles of the Example each had ahigher permeability and an improved refrigerating performance. As aresult, it was found that the effect of the present invention could beexerted even if the material composition was changed.

INDUSTRIAL APPLICABILITY

According to the group of rare-earth regenerator material particles ofthe present invention, it is possible to ensure the high-density fillingand attain a larger contact surface area between the group ofregenerator material particles and the operating medium gas such as Hegas. Therefore, it is possible to improve the characteristics of therefrigerator using the group of rare-earth regenerator materialparticles, further the characteristics of the measuring apparatus usingthe refrigerator.

According to the method for manufacturing a group of rare-earthregenerator material particles of the present invention, it is possibleto effectively manufacture the group of rare-earth regenerator materialparticles of the present invention. By using the rare-earth regeneratormaterial particles of the present invention, it is possible to form thegroup of rare-earth regenerator material particles effectively.

DESCRIPTION OF SYMBOLS

-   1 rare-earth regenerator material particles    -   (rare-earth cold accumulating material particles)-   2 channel-shaped depressed portion-   3 hole-shaped depressed portion-   9 cooling chamber-   10 disk-shaped rotary body-   11 ladle-   12 molten metal-   13 pouring nozzle-   14 (group of) rare-earth regenerator material particles-   15 particle collection vessel-   30 GM refrigerator-   31 vacuum chamber-   32, 33 external cylinder-   34 first regenerator container-   35 second regenerator container-   36 Cu mesh material-   1C second group of regenerator material particles-   37 compressor-   38, 39 seal ring-   40 first expanding chamber-   41 second expanding chamber-   42 first cooling stage-   43 second cooling stage-   44 resistance thermometer-   45 heater

The invention claimed is:
 1. A Gifford MacMahon type (GM) refrigeratorfor accumulating an extremely low temperature cold, comprising: a vacuumchamber; an external cylinder provided so as to be disposed in thevacuum chamber, the external cylinder enclosing an inner space; at leastone regenerator container for accumulating cold which is arranged at theinner space inside the external cylinder; a seal ring installed betweenthe external cylinder and the regenerator container; an expandingchamber formed between the external cylinder and the regeneratorcontainer; a compressor for compressing a cooling medium gas; and agroup of regenerator material particles packed in the regeneratorcontainer; wherein the group of regenerator material particles have anaverage particle size of 0.045 to 3 mm, wherein a proportion ofparticles having a ratio of a long diameter to a short diameter of 2 orless is 90% or more by number, a proportion of particles having adepressed portion having a length of 1/10 to ½ of a particlecircumferential length of a particle on a particle surface is 30% ormore by number and wherein the depressed portion has a depth of 1/10 orless of a particle diameter.
 2. The GM refrigerator for accumulating anextremely low temperature cold according to claim 1, wherein two or morestages of regenerator material-filled zones are formed through a meshmaterial in at least one regenerator container, and the group ofregenerator material particles are packed in at least one stage of theregenerator material-filled zones.
 3. GM refrigerator for accumulatingan extremely low temperature cold according to claim 2, wherein metalmesh-like members as the mesh material are packed in at least one stageof the regenerator material-filled zones.
 4. The GM refrigerator foraccumulating an extremely low temperature cold according to claim 3,wherein the mesh material comprising a mesh-like member composed ofcopper or a copper alloy is packed.
 5. The GM refrigerator foraccumulating an extremely low temperature cold according to claim 3,wherein the metal mesh-like members are packed in a regeneratormaterial-filled zone which is located at a high temperature side thanthe regenerator material-filled zone into which the regenerator materialparticles are packed.
 6. The GM refrigerator for accumulating anextremely low temperature cold according to claim 1, wherein two or moreregenerator containers are connected.
 7. The GM refrigerator foraccumulating an extremely low temperature cold according to claim 6,wherein the regenerator further comprises a mesh material comprising ametal mesh-like member composed of copper or a copper alloy.
 8. The GMrefrigerator for accumulating an extremely low temperature coldaccording to claim 1, wherein the refrigerator is used for forming anextremely low temperature cold zone having a temperature of lower than10K.
 9. The GM refrigerator for accumulating an extremely lowtemperature cold according to claim 1, wherein the group of regeneratormaterial particles comprises at least one element selected from a groupconsisting of yttrium (Y), lanthanum (La), Cecerium (Ce), praseodymium(Pr), neodymium (Nd), promethium (Pm), samarium (Sm), europium (Eu),gadolinium (Gd), terbium (Tb), dysprosium (Dy), holmium (Ho), erbium(Er), thulium (Tin), and ytterbium (Yb).
 10. The GM refrigerator foraccumulating an extremely low temperature cold according to claim 1,wherein the group of regenerator material particles comprise at leastone substance selected from a group consisting of a rare-earth elementof single substance, and alloy with Cu (including an intermetalliccompound), a rare-earth with Ni (including an intermetallic compound), arare-earth oxide (including a rare-earth complex oxide), and arare-earth sulfide.
 11. The GM refrigerator for accumulating anextremely low temperature cold according to claim 1, wherein theregenerator material particles comprise at least one substance selectedfrom the group consisting of Nd, Er3Ni, ErNi, HoCu2, Gd2O3 and Gd2O2S.12. A superconducting magnet provided with a refrigerator foraccumulating an extremely low temperature cold, wherein the refrigeratoris a GM refrigerator according to claim
 1. 13. A measuring apparatusprovided with a refrigerator for accumulating an extremely lowtemperature cold, wherein the refrigerator is a GM refrigeratoraccording to claim
 1. 14. An MRI provided with a refrigerator foraccumulating an extremely low temperature cold, wherein the refrigeratoris a GM refrigerator according to claim
 1. 15. An NMR provided with arefrigerator for accumulating an extremely low temperature cold, whereinthe refrigerator is a GM refrigerator according to claim
 1. 16. Acryopump provided with a refrigerator for accumulating an extremely lowtemperature cold, wherein the refrigerator is a GM refrigeratorcomprising the GM regenerator according to claim
 1. 17. A pulse tuberefrigerator comprising: at least one regenerator unit; and a group ofregenerator material particles packed in the at least one regeneratorunit, wherein the group of regenerator material particles have anaverage particle size of 0.045 to 3 mm, wherein a proportion ofparticles having a ratio of a long diameter to a short diameter of 2 orless is 90% or more by number, a proportion of particles having adepressed portion having a length of 1/10 to ½ of a particlecircumferential length of a particle on a particle surface is 30% ormore by number and wherein the depressed portion has a depth of 1/10 orless of a particle diameter.
 18. The pulse tube refrigerator accordingto claim 17, wherein the pulse tube refrigerator is a two-staged pulsetube refrigerator comprising two regenerator units.
 19. The pulse tuberefrigerator according to claim 17, wherein the pulse tube refrigeratoris a multi-staged pulse tube refrigerator comprising two or moreregenerator units.
 20. A superconducting magnet provided with arefrigerator for accumulating an extremely low temperature cold, whereinthe refrigerator is the pulse tube refrigerator according to claim 17.21. A measuring apparatus provided with a refrigerator for accumulatingan extremely low temperature cold, wherein the refrigerator is the pulsetube refrigerator according to claim
 17. 22. An MRI provided with arefrigerator for accumulating an extremely low temperature cold, whereinthe refrigerator is the pulse tube refrigerator according to claim 17.23. An NMR provided with a refrigerator for accumulating an extremelylow temperature cold, wherein the refrigerator is the pulse tuberefrigerator according to claim
 17. 24. A cryopump provided with arefrigerator for accumulating an extremely low temperature cold, whereinthe refrigerator is the pulse tube refrigerator according to claim 17.